Many friends who want to produce industrialized must be unfamiliar with Jet Mill of Atomized Feni50. Jet Mill of Atomized Feni50 has a very convenient, crushing speed, and quality of crushing product. It is a very useful crushing machine. .
Jet Mill of Atomized Feni50 has a wide range of pulverized granularity, simple and convenient, but during the pulverization process, there is often a case where the crushing effect is different.
The crushing effect is mainly affected by the following factors:
The temperature and pressure of the gas ratio, the feed particle size, the working fluid, and the pulverization aid. The gas-solid ratio of the pulverizer in crush is an important technical parameter and an important indicator. If the gas is too small, the kinetic energy of the airflow will be insufficient, which will affect the fineness of the product. But if the gas is too high, not only will waste energy, but will even degrade the dispersion performance of certain pigments. When pulverizing hard materials, there is a stricter requirement for the particle size of the feed. In terms of titanium powder, it is necessary to control 100 to 200 mesh when pulverizing calcination; the material after pulverizing surface is generally 40 to 70 mesh, and cannot exceed 2 to 5 mesh. So, should you choose how high pressure when crushing? Those skilled, this is mainly dependent on the comminutability and fineness requirements of the material.
Jet Mill Of Atomized Feni50 has many core accessories, and these attachments are also fragile parts. Once they don't pay attention to repair, it will cause serious consequences, especially if the gas flow grinding spindle will cause downtime, and cannot estimate the output loss. The following sections describe the reasons why the airflow grinding principal beam fracture is described.
The cause of the airflow grinding main shaft is easy to damage: 1. Since the pulverizer is a long-time crushing and ground bulk ore, the mechanical impact will cause fatigue damage to the spindle, if it is operated, the surface of the spindle Will wear, if you don't pay attention, cracks are generated.
2. The air supply will pass the airflower overload. When air flow is blockedWhen used, you need to feed properly, and the workload of each machine is limited. If this is exceeded, the component is easily damaged in the load operation, which will affect the overall service life of the airflow.
3. During mining and transportation, ore is often mixed with some waste metals. When these objects are in electromagnets at the upper portion of the belt, the electromagnet cannot be Excluding, causing these materials in ore and mud into gas flow, resulting in frequent iron, resulting in frequent impact on the spindle and other portions.
The above is why Jet Mill Of Atomized Feni50 spindle is easily damaged.
ALPA Battery Jet Mill Of Atomized Feni50 Case Sharing:
The company has advanced technology and excellent quality, and has established a complete quality management operation system.
Case parameters
Product particle size: D50: 15μm
hour yield: 600kg
To understand more product knowledge, you can continue to pay attention to our website. If you need to buy Jet Mill Of Atomized Feni50, please feel free to contact us.